Derived from the Technology Development Mountain of NASA's Space Program (PARSEC®) PARSEC® Space metal foil has excellent insulation, moisture-proof, and thermal insulation effects, and is widely used in national sports venues, national grain depots, commercial buildings, residential, agricultural, and industrial buildings.
(PARSEC®)PARSEC® Space metal foil has excellent insulation, moisture-proof, and thermal insulation effects, and is widely used in national sports venues, national grain depots, commercial buildings, residential, agricultural, and industrial buildings. PARSEC® Space metal foil can highly reflect and block radiation heat, while possessing extremely strong tension and will not deform, saving construction costs and manpower. It is a high-quality energy-saving product with the latest technology. PARSEC® Space metal foil system continues to expand to other applications and actively develops its characteristics.
| Testing items | Testing result | Testing standards |
| Near infrared reflectance | ± 95% (double sided) | （ASTM C1371-98） |
| Longitudinal tensile strength | 37Mpa | （JC/T 2290-2014） |
| Transverse tensile strength | 38Mpa | （JC/T 2290-2014） |
| Nail rod tear strength - longitudinal | 139N | （JC/T 2290-2014） |
| Nail rod tear strength - transverse | 115N | （JC/T 2290-2014） |
| Low temperature bending | -20℃, No cracks | （JC/T 2290-2014） |
| Impermeability | 0.3Mpa, no leakage for 30 minutes | （JC/T 2290-2014） |
| Hot air aging - longitudinal tension （80℃/168h） |
38Mpa | （JC/T 2290-2014） |
| Hot air aging - lateral tension （80℃/168h） |
40Mpa | （JC/T 2290-2014） |
| Hot air aging - elongation rate at maximum longitudinal force （80℃/168h） |
9% | （JC/T 2290-2014） |
| Hot air aging - elongation rate at maximum lateral force （80℃/168h） |
10% | （JC/T 2290-2014） |
| thermal conductivity | 0.035W/（m, k） (Containing 50mm thick rock wool with a unit weight of 120K) |
（GB/T 10295-2008） |
| Surface flame resistance | 1 level | （BS 476 Part 7） |
| Flame spread | 0 level | （BS 476 Part 6） |
| Water vapor permeability | 0.019 g/square meter/day | （ASTM E96 ProcedureA） |
| Salt spray test | no effect | （MTL-STD-810 Method 507） |
| Moisture test | no effect | （MTL-STD-810 Method 509） |
| Acid resistance | unchanged | 5% HCL impregnated surface for 48 hours 2% HCL impregnation surface for 168 hours |
| Weight and dimensions | Size: 1.25mX96mx0.15mm Roll weight: ± 22kg |